                  環保型聚氯乙烯耐遷移料 W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
                  Lead-free Migration Resistant PVC Compound...
                  型號:0

                  參考價:¥

                  說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
                  Product Description產品描述
                  Lead-free migration resistant PVC compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
                  環保型聚氯乙烯耐遷移料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、特種穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
                   
                  Characteristics and Application 特點及用途
                  The products have excellent migration-resistant properties and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of wire and cables which have anti-PS or anti-ABS property requirements.
                  產品具有良好的非遷移性,加工性能優異,符合RoHS環保標準。主要用于耐PS或ABS電線電纜絕緣和護套。
                   
                  Processing Indicator加工工藝
                  Recommend to use single-screw extruders with L/D= 20-25.
                  建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
                  Model
                  牌號
                  Machine Barrel Temperature
                  機筒溫度
                  Molding Temperature
                  機頭溫度
                  W-7091 / W-9091 / W-0591 150-175℃ 170-185℃
                  W-7092 / W-9092 / W-0592 150-175℃ 170-180℃
                   
                   
                  Physical and Electrical Properties
                  機械物理性能及電性能指標

                  Item

                  試驗項目

                  Unit
                  單位
                  Technical Requirements
                  技術要求
                  W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
                  Tensile Strength
                  拉伸強度
                  MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
                  Elongation at Break
                  斷裂伸長率
                  % ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
                  Thermal Deformation
                  熱變形
                  % ≤40 ≤50 ≤40 ≤50 ≤40 ≤50
                  Brittle Temperature with Impact
                  沖擊脆化溫度
                  -15 -20 -15 -20 -15 -20
                  200℃Thermal Stability
                  200℃時熱穩定時間
                  min ≥60 ≥60 ≥80 ≥80 ≥80 ≥80
                  20℃Volume Resistivity
                  20℃時體積電阻率
                  Ω.m ≥1.0×1011 ≥1.0×108 ≥1.0×1011 ≥1.0×109 ≥1.0×1011 ≥1.0×109
                  Dielectric Strength
                  介電強度
                  MV/m ≥20 ≥18 ≥20 ≥18 ≥20 ≥18
                  Thermal Aging
                  熱老化試驗
                  \ 100℃×168h 100℃×168h 100℃×240h 100℃×240h 135℃×168h 135℃×168h
                  Tensile strength after aging
                  老化后拉伸強度
                  MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
                  Tensile Strength Variation
                  拉伸強度變化率
                  % ±20 ±20 ±20 ±20 ±20 ±20
                  Elongation After Aging
                  老化后斷裂伸長率
                  % ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
                  Elongation Variation
                  斷裂伸長率變化率
                  % ±20 ±20 ±20 ±20 ±20 ±20
                  Migration ResistantTest
                  耐遷移試驗
                  (55℃×168h)
                  \ 無污染 無污染 無污染 無污染 無污染 無污染