                  環保型聚氯乙烯/丁腈復合物彈性體護套料 W-7081 W-9081 W-0581
                  Lead-free Elastomeric PVC / NBR Jacketing Compound...
                  型號:0

                  參考價:¥

                  說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
                  Product Description產品描述
                  Lead-free elastomeric PVC/NBR jacketing compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin and nitrile-butadiene rubber as the basic raw material, and add special plasticizer, stabilizer, flame retardant and other accessory ingredients.
                  環保型聚氯乙烯/丁腈復合物彈性體護套料是以優質聚氯乙烯樹脂和丁腈橡膠為基料,加入特種增塑劑、穩定劑、阻燃劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
                   
                  Characteristics and Application 特點及用途
                  These products have good oil-resistant property, soft and flexible, and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of oil-resistant and flame-retardant cables, elevator cables, oil-resistant soft wires of dust cleaner, heavy soft cables and crane cables.
                  產品具有良好的耐油性、彈性和柔軟性,加工性能優異,符合RoHS環保標準。主要用于有耐油要求的電線電纜、電梯電纜、耐油吸塵器軟線、重型軟線、起重機電纜等護層材料。
                   
                  Processing Indicator加工工藝
                  Recommend to use single-screw extruders with L/D= 20-25.
                  建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
                  Model
                  牌號
                  Machine Barrel Temperature
                  機筒溫度
                  Molding Temperature
                  機頭溫度
                  W-7081 / W-9081 / W-0581 145-170℃ 165-175℃
                   

                  Physical and Electrical Properties
                  機械物理性能及電性能指標

                  Item

                  試驗項目

                  Unit
                  單位
                  Technical Requirements
                  技術要求
                  W-7081 W-9081 W-0581
                  Density
                  比重
                  \ ≤1.35 ≤1.35 ≤1.35
                  Tensile Strength
                  拉伸強度
                  MPa ≥12.5 ≥12.5 ≥12.5
                  Elongation at Break
                  斷裂伸長率
                  % ≥250 ≥250 ≥250
                  Thermal Aging
                  熱老化試驗
                  \ 80℃×168h 100℃×240h 135℃×168h
                  Tensile Strength Variation
                  拉伸強度變化率
                  % ±40 ±40 ±40
                  Elongation Variation
                  斷裂伸長率變化率
                  % ±40 ±40 ±40
                  Dielectric Strength
                  介電強度
                  MV/m ≥18 ≥18 ≥18
                  200℃Thermal Stability
                  200℃時熱穩定時間
                  min ≥80 ≥120 ≥120
                  20℃Volume Resistivity
                  20℃時體積電阻率
                  Ω.m ≥1×108 ≥1×108 ≥1×108
                  Brittle Temperature with Impact
                  沖擊脆化溫度
                  -35 -35 -35
                  Oil Resistance
                  耐油性能(ASTM 902)
                  Temperature of Test試驗溫度 70 100 100
                  Time of Test
                  試驗時間
                  h 24 24 24
                  Tensile Strength Variation
                  拉伸強度變化率
                  % ±40 ±40 ±40
                  Elongation Variation
                  斷裂伸長率變化率
                  % ±40 ±40 ±40
                  Hardness
                  硬度
                  Shore A ≤70 ≤70 ≤70