                  您所在的位置:網站首頁 > > 產品中心 > 彈性體材料 > PVC彈性體環保型聚氯乙烯彈性體阻燃護套料 W-7326 W-9326 W-05326
                  環保型聚氯乙烯彈性體阻燃護套料 W-7326 W-9326 W-05326
                  Lead-free Elastomeric Flame Retardant PVC Jacketing Compound...
                  型號:0

                  參考價:¥

                  說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
                  Product Description產品描述
                  Lead-free elastomeric flame retardant PVC jacketing compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add plasticizer, stabilizer, flame retardant and other accessory ingredients.
                  環保型聚氯乙烯彈性體阻燃護套料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑、阻燃劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
                   
                  Characteristics and Application 特點及用途
                  These products have excellent mechanical and physical properties, soft and flexible, good processability. They meet RoHS Standard. They are mainly used for the jacketing of oil-resistant and flame-retardant cables, elevator cables, oil-resistant soft wires of dust cleaner, heavy soft wires, crane cables and so on.
                  產品具有良好的機械物理性能、彈性和柔軟性,加工性能優異,符合RoHS環保標準。主要用于有耐油和阻燃要求的電線電纜、電梯電纜、耐油吸塵器軟線、重型軟線、起重機電纜等護層材料。
                   
                  Processing Indicator加工工藝
                  Recommend to use of single-screw extruders with L/D= 20-25.
                  建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
                  Model
                  牌號
                  Machine Barrel Temperature
                  機筒溫度
                  Molding Temperature
                  機頭溫度
                  W-7326 / W-9326 / W-05326 165-170℃ 175-185℃
                   
                   
                  Physical and Electrical Properties
                  機械物理性能及電性能指標

                  Item

                  試驗項目

                  Unit
                  單位
                  Technical Requirements
                  技術要求
                  W-7326 W-9326 W-05326
                  Density
                  比重
                  \ ≤1.45 ≤1.45 ≤1.45
                  Oxygen Index
                  氧指數
                  % ≥28 ≥28 ≥28
                  Tensile Strength
                  拉伸強度
                  MPa ≥12.5 ≥12.5 ≥12.5
                  Elongation at Break
                  斷裂伸長率
                  % ≥250 ≥250 ≥250
                  200℃Thermal Stability
                  200℃時熱穩定時間
                  min ≥80 ≥80 ≥80
                  20℃Volume Resistivity
                  20℃時體積電阻率
                  Ω.m ≥1×108 ≥1×108 ≥1×108
                  Dielectric Strength
                  介電強度
                  MV/m ≥18 ≥18 ≥18
                  Brittle Temperature with Impact
                  沖擊脆化溫度
                  -40 -40 -40
                  Hardness
                  硬度
                  Shore A ≤75 ≤75 ≤78
                  Thermal Aging
                  熱老化試驗
                  / 100℃×168h 100℃×240h 135℃×168h
                  Tensile Strength Variation
                  拉伸強度變化率
                  % ±30 ±30 ±30
                  Elongation Variation
                  斷裂伸長率變化率
                  % ±30 ±30 ±30
                  Oil Resistance
                  耐油性能(ASTM 902)
                  Temperature of Test試驗溫度 70 70 70
                  Time of Test
                  試驗時間
                  h 4 4 4
                  Tensile Strength Variation
                  拉伸強度變化率
                  % ±30 ±30 ±30
                  Elongation Variation
                  斷裂伸長率變化率
                  % ±30 ±30 ±30