                  Product Description 產品描述
                  105℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients. This product has excellent mechanical and physical properties, electrical property and good processability. It can meet RoHS Standard. The cables with it can meet LV112, VW60306, DIN72551 and other related standards. The highest working temperature is 105℃.
                  環保型105℃汽車原線料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。產品具有良好的機械物理性能和電性能,加工性能優異,符合RoHS環保標準。制成電線后可以滿足LV 112、VW 60306、DIN 72551等相關標準,最高工作溫度為105℃。
                   
                  Product Details  產品明細
                  Model
                  牌號
                  Application
                  用途
                  W-0596 >16mm2cables
                  16mm2以上規格的電線
                  W-0597 0.5mm2 ~6mm2 cables
                  0.5mm2 ~6mm2及以規格的電線
                  W-0598 ≤ 0.5mm2 cables
                  0.5mm2及以下規格的電線
                   
                   
                  Processing Indicator 加工工藝
                  Recommend to use of single-screw extruders with L/D= 20-25.
                  建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
                  Model
                  牌號
                  Machine Barrel Temperature
                  機筒溫度
                  Molding Temperature
                  機頭溫度
                  W-0596 / W-0597 165-185℃ 180-190℃
                  W-0598 165-185℃ 185-190℃
                   
                   
                  Physical and Electrical Properties 機械物理性能及電性能指標

                  Item

                  試驗項目

                  Unit
                  單位
                  Molding Temperature
                  技術要求
                  W-0596 W-0597 W-0598
                  Density
                  比重
                  \ 1.32±0.02 1.32±0.02 1.32±0.02
                  Tensile Strength
                  拉伸強度
                  MPa ≥18.0 ≥18.0 ≥18.0
                  Elongation at Break
                  斷裂伸長率
                  % ≥250 ≥250 ≥250
                  200℃Thermal Stability
                  200℃時熱穩定時間
                  min ≥200 ≥200 ≥200
                  20℃Volume Resistivity
                  20℃時體積電阻率
                  Ω.m ≥1×1011 ≥1×1011 ≥1×1011
                  Dielectric Strength
                  介電強度
                  MV/m ≥22 ≥20 ≥20
                  Brittle Temperature with Impact
                  沖擊脆化溫度
                  -25 -25 -25
                  Hardness
                  硬度
                  Shore A 88±2 94±2 97±2
                  Thermal Aging
                  熱老化試驗
                  \ 136℃×168h
                  Tensile Strength Variation
                  拉伸強度變化率
                  % ±20 ±20 ±20
                  Elongation Variation
                  斷裂伸長率變化率
                  % ±20 ±20 ±20